China wholesale ethyl acetate - Water-based two-component varnish two component water based polyurethane waterproof coating from China – Mit-ivy
China wholesale ethyl acetate - Water-based two-component varnish two component water based polyurethane waterproof coating from China – Mit-ivy Detail:
Application
Recommended use for storage tanks, rail transportation, functional vehicles, power facilities, transformers, distribution cabinets, machinery and equipment such as high anti-corrosion and decorative coating.
Technical parameters Drying time (25′℃) Surface drying 1 hour
Hands-on 24 hours
Drying 1 hour (60-80°C)
Fully cured 7 days
Gloss ≥80% (60°)
Film hardness H
Paint film adhesion level 4
Paint film flexibility 2mm
Impact resistance of paint film 50cm-kg
Artificial aging resistance 1000h
Surface treatment When directly applied on the surface of the primer, the primer shall be polished, clean, dry, free of rust and oil stains. When coated on the surface of the primer, the primer surface should be clean, dry and free of dirt.
Use conditions Construction temperature 10-35 ℃, mixing degree 30-75%, good ventilation conditions.
Construction instructions Ingredients A, B two components
Mixing ratio 3:1 (weight ratio)
Mixing method: Mix component A thoroughly, add component B and continue mixing until smooth.
Coating thickness Dry film thickness 20 μ m
Wet film thickness 50 μ m
Maturing period (25℃) 10-15min
Service period (25°C) 3h
Re-coating interval 12h minimum 4Bh maximum
Surface Treatment The front coat paint reading must be dry.
Remove all oil, dust and other dirt from the front paint film. No acid, breakage or water congealed on the paint film.
Quick Details
For the topcoat that has been circled for a long time, the paint film should be polished with sandpaper before painting the subsequent topcoat.
Temperature of the substrate The temperature of the substrate should be 3℃ above the dew point.
Coating Method Air Spray Thinner Deionized Water
Dilution amount 15-25% (paint volume note)
Nozzle diameter 1.5-2.0m
Spraying pressure 0.3-0.4Mpa (about 3-6kg/cmi)
【Color Water Paint Application Viscosity 15-25s (20℃℃)
Waterborne two-component polyurethane topcoats
This product is made up of non-New Tongkou Nagasumi System, regional chemical new, surface ionized water, woody with N, and bad protective compound, and does not contain organic solvents such as methyl-phthalate and 3% lysine.
1. low V0C, no irritating odor.
Environmentally labeled products, no health risks from normal use.
Outstanding resistance to a wide range of weather conditions and operating environments, excellent UV resistance.
After curing, the paint film is tough and has excellent abrasion and impact resistance.
When used in conjunction with a water-based primer, it can withstand the effects of aggressive industrial environments.
Product detail pictures:
Related Product Guide:
CAS No. [95-68-1] Production process. 2,4-Dimethylaniline
List of flammable and explosive chemical reagents commonly used in laboratories
It is actually our accountability to satisfy your needs and effectively serve you. Your pleasure is our best reward. We're on the lookout forward for your stop by for joint growth for China wholesale ethyl acetate - Water-based two-component varnish two component water based polyurethane waterproof coating from China – Mit-ivy , The product will supply to all over the world, such as: Serbia, Sydney, Costa Rica, We supply skilled service, prompt reply, timely delivery, excellent quality and best price to our customers. Satisfaction and good credit to every customer is our priority. We focus on every detail of order processing for customers till they have received safe and sound items with good logistics service and economical cost. Depending on this, our products and solutions are sold very well in the countries in Africa, the Mid-East and Southeast Asia. Adhering to the business philosophy of ??customer first, forge ahead', we sincerely welcome clients from at home and abroad to cooperate with us.
By Amber from Birmingham - 2017.08.18 18:38
Customer service staff and sales man are very patience and they all good at English, product's arrival is also very timely, a good supplier.
By Roberta from Israel - 2017.01.11 17:15